Integrating Dy-DOTA motifs into mesoporous silica nanoparticle scaffolds generates remarkable ultrahigh field T2 relaxivities for a well-defined and tailorable contrast agent, attributed to enhanced Curie outer-sphere contributions as supported by simulation.